This work is devoted to the study of magnetic Fe3O4 nanoparticles doubly coated with carbon. First, Fe3O4@C nanoparticles were synthesized by thermal decomposition. Then these synthesized nanoparticles, 20-30 nm in size were processed in a solution of glucose at 200 °C during 12 h, which led to an unexpected phenomenon-the nanoparticles self-assembled into large conglomerates of a regular shape of about 300 nm in size. The morphology and features of the magnetic properties of the obtained hybrid nanoparticles were characterized by transmission electron microscopy, differential thermo-gravimetric analysis, vibrating sample magnetometer, magnetic circular dichroism and Mössbauer spectroscopy. It was shown that the magnetic core of Fe3O4@C nanoparticles was nano-crystalline, corresponding to the Fe3O4 phase. The Fe3O4@C@C nanoparticles presumably contain Fe3O4 phase (80%) with admixture of maghemite (20%), the thickness of the carbon shell in the first case was of about 2-4 nm. The formation of very large nanoparticle conglomerates with a linear size up to 300 nm and of the same regular shape is a remarkable peculiarity of the Fe3O4@C@C nanoparticles. Adsorption of organic dyes from water by the studied nanoparticles was also studied. The best candidates for the removal of dyes were Fe3O4@C@C nanoparticles. The kinetic data showed that the adsorption processes were associated with the pseudo-second order mechanism for cationic dye methylene blue (MB) and anionic dye Congo red (CR). The equilibrium data were more consistent with the Langmuir isotherm and were perfectly described by the Langmuir-Freundlich model.
RESUMO
Characterization of magnetic particulate matter (PM) in coal fly ashes is critical to assessing the health risks associated with industrial coal combustion and for future applications of fine fractions that will minimize solid waste pollution. In this study, magnetic narrow fractions of fine ferrospheres related to environmentally hazardous PM2.5, PM2.5-10, and PM10 were for the first time separated from fly ash produced during combustion of Ekibastuz coal. It was determined that the average diameter of globules in narrow fractions is 1, 2, 3, and 7 µm. The major components of chemical composition are Fe2O3 (57-60) wt %, SiO2 (25-28 wt %), and Al2O3 (10-12 wt %). The phase composition is represented by crystalline phases, including ferrospinel, α-Fe2O3, ε-Fe2O3, mullite, and quartz, as well as the amorphous glass phase. Mössbauer spectroscopy and magnetic measurements confirmed the formation of nanoscale particles of ε-Fe2O3. Stabilization of the ε-Fe2O3 metastable phase, with quite ideal distribution of iron cations, occurs in the glass matrix due to the rapid cooling of fine globules during their formation from mineral components of coal.